DESCRIPTION:

AT-PU FLEX is a hydrophilic polyurethane based foam resin used for injection into concrete structures exhibiting water seepages. AT-PU FLEX is a single component hydrophilic resin that reacts to form a flexible closed cell foam or gel depending on the amount of water it comes in contact with. Due to its flexible property, AT-PU FLEX is an ideal choice of material for mitigating water ingress through RCC members that are likely to be subjected to dynamic loadings, thermal expansion/contractions and other associated movements

USES:

  • AT-PU FLEX is used to stop water ingress through concrete elements such as basement podium slabs, parking structures slabs, waffle slabs, roof slabs, sewage treatment plants, tunnel linings etc.

ADVANTAGES:

  • Flexible closed cell gel / foam

TYPICAL APPLICATION:

  • Sealing against water ingress
  • Sealing against leaking cracks and joints
  • Sealing against water in masonry and brickwork
  • Void filling
  • Back grouting

INJECTION PROCESS:

  • Identify the area to be injected. Install injection packers of suitable diameter and length. Ensure injection packers are tightly installed to avoid packer failure during injection process. If required, seal packers using quick setting cement or epoxy based putty. Feed the resin into the pump and commence injection. Injection pressure shall be governed by the type of element, effective water head, packer spacing and other factors. For injection below raft slab, grade slab and retaining walls inject in intermittent batches and observe effect. Avoid large volume injections in short period.
  • Adaptable reaction time is possible by varying the catalyst [AT-PU FLEX (K)] ratio from between 2% to 10%.

TECHNICAL DATA :

MATERIAL DESCRIPTION Single component solvent free polyurethane injection resin curing to form a flexible form/gel
APPEARANCE Light yellow clear liquid
VISCOCITY ~ 1000 cps (@ 23ºC)
DENSITY ~ 1.10 g/cm³ (@ 23ºC)
VOLUME EXPANSION Up to 15 times (Resin : Water = 10 : 1) @ 25ºC
REACTION TIME Up to 180 seconds (depending on temperature)
POT LIFE Up to 30 minutes @ 23ºC (surface film that forms upon humidity contact to be discarded and not mixed in)
APPLICATION TEMPREATURE › 5ºC (substrate temperature during injection)
APPLICATION EQUIPEMENT SD-1L or suitable single component positive displacement resin injection pump capable of developing required injection pressures. Non-return injection packers.

TECHNICAL SPECIFICATION OF AT-PU FLEX (K):

COLOUR Clear to yellowish
VISCOCITY ~ 70 cps (@ 23ºC)
DENSITY ~ 1.10 g/cm³ (@ 20ºC)

TESTING OF AT-PU FLEX (K):

  • All tests were carried out using the following Mixing Ratio
    • AT-PU FLEX : 100 parts by Weight
    • AT-PU FLEX (K) : 10% of AT-PU FLEX by Weight
    • Water : In all tests 10% by Weight
REACTION TIMES WITH 10% WATER & 10% ACCELERATOR
Initial Temperature (°C)5 10 15 20
Start Reaction (sec)120 60 25 10
End Reaction (sec)300 200 110 50
Foam Expansion Rate (approx)25 25 25 30

(All technical data stated herein is based on tests carried out under laboratory conditions.)
PACKAGING & STORAGE:

  • AT-PU FLEX is available in 10 kg HDPE Pack
  • AT-PU FLEX (K) is available in 1 kg HDPE Pack
  • Shelf life is 6 months in sealed containers as provided
  • Keep containers sealed and away from heat and cold in a well ventilated area (5ºC to 30ºC)

HEALTH & SAFETY:

  • Protect hands with rubber gloves and eyes with goggles.
  • Accidental splashes to the skin or eyes must be rinsed immediately with clean water.
  • Store in well-labeled containers.
  • Non dangerous goods, please observe Material Safety datasheet.